FRAGOM LCX/3013
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | FRAGOM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FOW6Ga_FRAGOM-LCX-3013.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FRAGOM G LCX/3013 is a flame retardant halogen free polyolefin compound. FRAGOM G LCX/3013 is a halogen-free flame-retardant partially crosslinked compound suitable for automotive cables insulation and low voltage insulation. To be used with 1-2% of catalyst MAC/202. The material doesn't pass abrasion test on cables sized less than 0.75 mm² having 0.25 mm thickness. Certify: SAE J1127/J1128,FIAT 7.Z8220 T3 -T3 S,ISO 6722 Class C,LV 112 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 1.0 to 2.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 51 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | > 15.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | > 200 | % | IEC 60811 |
| Abrasion Resistance 1(250.0 µm) | > 3.5E+2 | Cycles | LV 112 |
| Aging | Nominal Value | Test Method | |
|---|---|---|---|
| Heat Aging 2(175°C) | No Crack | IEC 60811 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | -40 to 125 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | < 0.100 | % | IEC 60754-1 |
| Oxygen Index | 25 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 2 Temp. | 185 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 210 | °C | |
| Cylinder Zone 5 Temp. | 220 | °C | |
| Die Temperature | 225 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | 0.75mm² Size |
| 2 . | 1 hr on Mandrel |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® CP 1011 | Plastic Solutions, Inc. | PP Impact Copolymer | PrimaFlex® |
| Clyrell RC2472 | LyondellBasell Industries | PP Random Copolymer | Clyrell |
| Ferro PP TPP40AC46BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Greenflex® HN 70 | Versalis S.p.A. | EVA | Greenflex® |
| Lupoy® 3010-30 | LG Chem Ltd. | PC | Lupoy® |