POLYFLAM® RPP 500 D
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FONMfi_POLYFLAM-RPP-500-D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant PP-homopolymer - standard grade without PBDE |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 10.0 | cm³/10min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 0.13 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 65.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 28.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 2.3 | kJ/m² | |
| 23°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 19 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact (Area) (23°C) | 4.00 | kJ/m² | ASTM D256 |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 2.5 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -40°C | 15 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 120 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 85.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ISO 306/A120 |
| -- | 94.0 | °C | ISO 306/B50 |
| Ball Pressure Test (130°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 750 | °C | |
| 1.50 mm | 725 | °C | |
| 3.00 mm | 725 | °C | |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PP Random Copolymer RP200 | M. Holland Company | PP Random Copolymer | MTEGRITY™ PP Random Copolymer |
| TRIREX® Compound 3025G15 | Samyang Corporation | PC | TRIREX® Compound |
| Nipol® 1312LV | Zeon Chemicals L.P. | NBR | Nipol® |
| Novodur® Ultra 4115 | Styrolution | PC+ABS | Novodur® Ultra |
| BESTNYL SE30VI02AWXL | Triesa Plastics | Nylon 66 | BESTNYL |