Order Products : sales@su-jiao.com
Ingeo™ 2500HP
| Category: | PLA , Polylactic Acid |
| Manufacturer: | NatureWorks® LLC |
| Trademark: | Ingeo™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FNUL20_Ingeo-2500HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ingeo 2500HP is a high viscosity product from NatureWorks LLC, designed for extrusion applications. It is designed to crystallize during processing, leading to higher heat deflection temperatures in opaque applications. The variety of products made with 2500HP is widely varied and growing. Applications include crystalline sheet for cards, graphic arts and signage. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | |||
| -- 1 | 1.7 - 1.8 | % | |
| -- 2 | 0.30 - 0.40 | % | |
| Relative Viscosity 3 | 4.0 | ASTM D5225 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield 4 | 65.5 | MPa | ASTM D638 |
| Yield 5 | 64.1 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Fracture 6 | 4.3 | % | ASTM D638 |
| Fracture 7 | 3.6 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| -- 8 | 4450 | MPa | ASTM D790 |
| -- 9 | 3640 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| -- 10 | 126 | MPa | ASTM D790 |
| -- 11 | 113 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -- 12 | 40 | J/m | ASTM D256 |
| -- 13 | 19 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM E2092 | ||
| 0.45 MPa, not annealed 14 | 144 | °C | ASTM E2092 |
| 0.45 MPa, not annealed 15 | 54.0 | °C | ASTM E2092 |
| Peak Crystallization Temperature (DSC) 16 | 180 | °C |
| Optical | Nominal Value | ||
|---|---|---|---|
| Clarity | |||
| -- 17 | Opaque | ||
| -- 18 | Transparent |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | < 0.025 | % | |
| Hopper Temperature | 45.0 | °C | |
| Cylinder Zone 1 Temp. | 191 | °C | |
| Cylinder Zone 2 Temp. | 199 | °C | |
| Cylinder Zone 3 Temp. | 210 | °C | |
| Adapter Temperature | 210 | °C | |
| Melt Temperature | 210 | °C | |
| Die Temperature | 210 | °C |
| Extrusion instructions |
|---|
| Screw Speed 20-150 rpmL/D ratios from 24:1 to 32:1Compression ratio of 2.5:1 to 3:1Note: Amorphous polymer must be dried below 120°F (50°C). |
| Note Message | |
|---|---|
| 1 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 2 . | Molded amorphous with 26°C mold temperature |
| 3 . | Measured at 1.0 g/dL in chloroform at 30°C |
| 4 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 5 . | Molded amorphous with 26°C mold temperature |
| 6 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 7 . | Molded amorphous with 26°C mold temperature |
| 8 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 9 . | Molded amorphous with 26°C mold temperature |
| 10 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 11 . | Molded amorphous with 26°C mold temperature |
| 12 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 13 . | Molded amorphous with 26°C mold temperature |
| 14 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 15 . | Molded amorphous with 26°C mold temperature |
| 16 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 17 . | Molded crystalline with 120°C mold temperature where formula included 1wt% nucleating agent (LAK-301 from Takemoto Oil & Fat) |
| 18 . | Molded amorphous with 26°C mold temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 251-85W232 | ExxonMobil Chemical | TPV | Santoprene™ |
| BESTNYL SI00VI02BEHX | Triesa Plastics | Nylon 6 | BESTNYL |
| Hysol® EA9437 | Loctite® | Epoxy | Hysol® |
| Karina WHITE PVC COMPOUND 807-10/236-H-ISE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ADLAS® N09FJB-00 | A.D. Compound S.p.A. | PP Homopolymer | ADLAS® |