HiPrene® M570
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | GS Caltex |
| Trademark: | HiPrene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FNMcel_HiPrene-M570.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiPrene® M570 is polypropylene impact copolymer with good processing stability and medium fluidity. It is intended especially for injection moulding of products where good impact resistance as well as high stiffness is required. This grade is available in different colors. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.910 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 40 | g/10 min | ASTM D1238 |
| Ash Content (600°C) | 1.0 | % | Internal method |
| Volatile Matter | 0.10 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 23.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus 1(23°C) | 1450 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 8.00 | kJ/m² | ASTM D256 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 4.00 - 6.50 | MPa |
| Injection instructions |
|---|
| Back Pressure: Low to MediumScrew Speed: Low to MediumInjection Speed: 100 to 200 m/min |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPSiV™ X5300 A 8506 NAT 25644 | Multibase, A Dow Corning Company | TPSiV | TPSiV™ |
| YUNGSOX® PP 2080 | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| Nanjing Hongrui PA66 A3010 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Grilamid® 2S 25 W 20 HL X nat | EMS-GRIVORY | Nylon 610 | Grilamid® |
| Epic Urethane S7356 | Epic Resins | PUR, Unspecified | Epic Urethane |