Lucky Enpla LGF5408A
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Lucky Enpla Co LTD |
| Trademark: | Lucky Enpla |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FNKUSZ_Lucky-Enpla-LGF5408A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lucky Enpla LGF5408A is a polyamide 66 (nylon 66) product that contains 40% glass \minerals. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Typical application areas are: automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 - 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 137 | MPa | ASTM D638 |
| Flexural Modulus 2 | 7650 | MPa | ASTM D790 |
| Flexural Strength 3 | 216 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (6.35 mm) | 54 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 235 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 250 - 270 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 260 - 280 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Back Pressure | 0.490 - 1.96 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 250-270°CInjection Pressure (1st Pressure): 800-1300 kg/cm²Injection Pressure (2nd Pressure): 500-800 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 3.0 mm/min |
| 3 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nymax™ GF 1200 A 33 HS Natural | PolyOne Corporation | Nylon 66 | Nymax™ |
| Alathon® M5010 | LyondellBasell Industries | HDPE | Alathon® |
| GAPEX® RPP25EB68HB GRAY | Ferro Corporation | PP Homopolymer | GAPEX® |
| Hanwha Total PP BJ352 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| Ipethene® 111 | Carmel Olefins Ltd. | LDPE | Ipethene® |