Sarlink® TPE ME-2385N
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FMxYd6_Sarlink-TPE-ME-2385N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE ME-2385N is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Sarlink®The main features of TPE ME-2385N are:
Sarlink®The typical application field of TPE ME-2385N is: automobile industry |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shore A, 1 second, injection molding | 86 | ISO 868 | |
| Shore A, 5 seconds, injection molding | 84 | ISO 868 | |
| Shore A, 15 seconds, injection molding | 81 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ISO 37 | ||
| Transverse flow : 100% strain | 3.62 | MPa | ISO 37 |
| Flow : 100% strain | 4.39 | MPa | ISO 37 |
| Tensile Stress 2 | ISO 37 | ||
| Transverse flow : Fracture | 13.8 | MPa | ISO 37 |
| Flow : Fracture | 9.10 | MPa | ISO 37 |
| Tensile Elongation 3 | ISO 37 | ||
| Transverse flow : Fracture | 830 | % | ISO 37 |
| Flow : Fracture | 620 | % | ISO 37 |
| Tear Strength 4 | ISO 34-1 | ||
| Transverse flow | 43 | kN/m | ISO 34-1 |
| Flow | 46 | kN/m | ISO 34-1 |
| Compression Set 5 | ISO 815 | ||
| 23°C, 22 hr | 20 | % | ISO 815 |
| 70°C, 22 hr | 32 | % | ISO 815 |
| 90°C, 70 hr | 37 | % | ISO 815 |
| 125°C, 70 hr | 49 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 6 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | -4.5 | % | ISO 188 |
| Flow : 110°C, 1008 hr | -14 | % | ISO 188 |
| Transverse flow : 100% strain 110°C, 1008 hr | 7.9 | % | ISO 188 |
| Flow : 100% strain 110°C, 1008 hr | 12 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | -2.9 | % | ISO 188 |
| Flow : 125°C, 168 hr | -18 | % | ISO 188 |
| Transverse flow : 100% strain 125°C, 168 hr | 6.9 | % | ISO 188 |
| Flow : 100% strain 125°C, 168 hr | 13 | % | ISO 188 |
| Change in Tensile Strain at Break in Air 7 | ISO 188 | ||
| Transverse flow : 110°C, 1008 hr | -3.6 | % | ISO 188 |
| Flow : 110°C, 1008 hr | -16 | % | ISO 188 |
| Transverse flow : 125°C, 168 hr | -4.7 | % | ISO 188 |
| Flow : 125°C, 168 hr | -20 | % | ISO 188 |
| Change in Shore Hardness in Air | ISO 188 | ||
| Support a, 110°C, 1008 hr 8 | 3.6 | ISO 188 | |
| Support a, 110°C, 1008 hr | 3.8 | ISO 188 | |
| Support a, 110°C, 1008 hr 9 | 2.7 | ISO 188 | |
| Support a, 125°C, 168 hr 10 | 3.4 | ISO 188 | |
| Support a, 125°C, 168 hr 11 | 3.1 | ISO 188 | |
| Support a, 125°C, 168 hr 12 | 2.5 | ISO 188 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 192 | Pa·s | ASTM D3835 |
| Additional Information |
|---|
| 雾化，3小时，100C，21C板 = 98% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | Type 1, 510mm/min |
| 2 . | Type 1, 510mm/min |
| 3 . | Type 1, 510mm/min |
| 4 . | B method, right angle specimen (without cut), 510mm/min |
| 5 . | Type a |
| 6 . | Type 1 |
| 7 . | Type 1 |
| 8 . | 5 sec |
| 9 . | 1 sec |
| 10 . | 15 sec |
| 11 . | 5 sec |
| 12 . | 1 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 HL NTLA010 NR310 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Andur AL 90 AP | Anderson Development Company | PUR-Eth,aliphat | Andur |
| ASTATAL™ F3054 | Marplex Australia Pty. Ltd. | Acetal (POM) Homopolymer | ASTATAL™ |
| Karina BLUE COLOR CONCENTRATE 06/595-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina BLUE PVC COMPOUND 75900-06/623-E-AC (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |