CYCOLOY™ EX39F resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FMLelE_CYCOLOY-EX39F-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Highest impact extrusion ABS for sheet and blow molding applications. FDA food contact compliant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.70 to 0.90 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1680 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 35.9 | MPa | |
| Break | 29.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 3.5 | % | |
| Break | 110 | % | |
| Flexural Modulus 4(50.0 mm Span) | 1900 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 57.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 320 | J/m | |
| 23°C | 460 | J/m | |
| Instrumented Dart Impact (23°C, Total Energy) | 39.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 91.7 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 77.8 | °C | |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 6 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.2E-4 | cm/cm/°C | |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI Str | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | HB | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (240°C, 100 sec^-1) | 1520 | Pa·s | ASTM D3835 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 1.0E-3 | % | |
| Cylinder Zone 1 Temp. | 193 to 210 | °C | |
| Cylinder Zone 2 Temp. | 199 to 221 | °C | |
| Cylinder Zone 3 Temp. | 204 to 232 | °C | |
| Cylinder Zone 4 Temp. | 210 to 235 | °C | |
| Adapter Temperature | 199 to 227 | °C | |
| Melt Temperature | 210 to 241 | °C | |
| Die Temperature | 210 to 241 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polylink Polymer PP 408-401-P-10040-B | Polylink Polymers (India) Ltd. | XLPE | Polylink Polymer |
| RTP 4406 L | RTP Company | Nylon, Unspecified | RTP |
| Sipolprene® 35180 W | SIPOL S.p.A | TPC-ET | Sipolprene® |
| TUFNYL® RGF 30 FRO GREY | SRF Ltd. | Nylon 66 | TUFNYL® |
| CGPC PVC SO-30X (80 phr Plasticizer D) | China General Plastics Corporation | PVC, Flexible | CGPC PVC |