VENELENE® 2706
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Poliolefinas Internacionales, C.A. (Polinter) |
| Trademark: | VENELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FMGHfO_VENELENE-2706.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features:
Applications:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.951 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (10% Igepal, F50) | 5.00 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 22.0 | MPa | |
| Break | 30.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 20 | % | |
| Break | > 1500 | % | |
| Flexural Modulus | 700 | MPa | ASTM D790 |
| Flexural Strength (5.0% Strain) | 20.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Impact | 100 | J/cm | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 210 to 240 | °C | |
| Mold Temperature | < 20.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® NB1803E-BK | Wellman Engineering Resins | Nylon+PP | Wellamid® |
| Vydyne® 66J | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| LNP™ THERMOCOMP™ Lexan_LGN2000A compound | SABIC Innovative Plastics Europe | PC | LNP™ THERMOCOMP™ |
| Eleme NGL070LG | Eleme Petrochemical Company Ltd | LLDPE | Eleme |
| OTECH PVC OW840 - Wire Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |