Hostalen PP H4122 103220
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FKnvbk_Hostalen-PP-H4122-103220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen PP H4122 103220 is a black coloured polypropylene blockcopolymer. The product has a high heat stability and extremely high extraction stability. The material Hostalen PP H4122 103220 has not been tested and therefore has not been certified for pressure applications. For further details about the suitable applications for this material please contact LyondellBasell. Hostalen PP H4122 103220 is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.908 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/5.0 kg | 0.50 | g/10 min | |
| 230°C/2.16 kg | 0.30 | g/10 min | |
| 230°C/5.0 kg | 1.3 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 66 | ISO 868 | |
| Ball Indentation Hardness (H 132/30) | 50.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 30.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 13 | % | ISO 527-2/50 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 1060 | MPa | |
| 1000 hr | 500 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.8 | kJ/m² | |
| 0°C | 18 | kJ/m² | |
| 23°C | 110 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 75.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 51.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 158 | °C | ISO 306/A50 |
| -- | 68.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 280 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® R019MZ | Reliance Industries Limited | PP Random Copolymer | REPOL® |
| Hanwha Total TPE SE75 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | TPE | Hanwha Total TPE |
| LNP™ LUBRICOMP™ UFL269SA compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |
| AURUM® JGN3030 | Mitsui Chemicals, Inc. | PI, TP | AURUM® |
| PONACOM ABS 7920 | Ponachem Compound GmbH | ABS | PONACOM ABS |