UMG ABS® FV700G6
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | UMG ABS, Ltd. |
| Trademark: | UMG ABS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FInlYG_UMG-ABS-FV700G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UMG ABS® FV700G6 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or North America for injection molding. Important attributes of UMG ABS® FV700G6 are:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.39 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 13.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.10 to 0.20 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 112 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7700 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 105 | MPa | ISO 527-2 |
| Flexural Modulus 1(23°C) | 8000 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 6.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 97.0 | °C | ISO 75-2/Af |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.50 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 190 to 210 | °C | |
| Middle Temperature | 200 to 220 | °C | |
| Front Temperature | 210 to 230 | °C | |
| Nozzle Temperature | 200 to 220 | °C | |
| Processing (Melt) Temp | 225 to 245 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 70.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 5.00 to 15.0 | MPa | |
| Screw Speed | 50 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC C8090 UVAF CL | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SCHULAMID® 66 MV 2 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Mowiflex™ FXT 283 | Kuraray Co., Ltd. | PVOH | Mowiflex™ |
| Adell Polyamide BR-13 | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| LNP™ STAT-KON™ DD000 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |