Nymax™ ND 1233 GF Black
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Nymax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FIBEbQ_Nymax-ND-1233-GF-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nymax of nylon 6/6 polymers reinforced with glass fibers®GF 1200 series products are specially used in harsh environments and have the characteristics of high rigidity, tensile properties, heat resistance, durability, etc. According to the needs of rigid characteristics, these materials have a large range of strength and are easy to process in standard thermoplastic processing equipment. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.39 | g/cm³ | ASTM D792 |
| -- | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 - 0.40 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 3.18 mm | 1.0 | % | ASTM D570 |
| 23°C, 24 hr | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 135 | MPa | ISO 527-2 |
| Fracture 1 | 145 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture 2 | 2.0 | % | ASTM D638 |
| Fracture | 2.0 - 4.0 | % | ISO 527-2 |
| Flexural Modulus | 9000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 230 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.18mm, injection molding | 64 | J/m | ASTM D256A |
| 23°C | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.18mm | 230 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 240 | °C | ISO 75-2/A |
| Peak Melting Temperature | 260 | °C | ASTM D789, ISO 3146 |
| Additional Information |
|---|
| Molded Test Bars: Dry as Molded |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Mold Temperature | 60.0 - 107 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP LW4406 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| VAMPLEN 1028 V0 | Vamp Tech | PP Homopolymer | VAMPLEN |
| Fainplast PVC RK 0758 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Halene L 71601W | Haldia Petrochemicals Ltd. | LLDPE | Halene L |
| Lion Idemitsu Composites PPS K531A1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |