Ateva® 1821A
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FHs28t_Ateva-1821A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is commonly used for coextrusion due to its superior sealability and strength. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 18.0 | wt% |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus - 1% Secant | 45.0 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D882A | ||
| MD : Break | 23.0 | MPa | |
| TD : Break | 27.0 | MPa | |
| Tensile Elongation 2 | ASTM D882A | ||
| MD : Break | 460 | % | |
| TD : Break | 620 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 59.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 87.0 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 210 | °C |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BESNO P40 TLX NL | Arkema | Nylon 11 | Rilsan® |
| Spartech Polycom SC5-3220 | Spartech Polycom | PP Homopolymer | Spartech |
| Witcom PP 5LG-EC | Witcom Engineering Plastics B.V. | PP, Unspecified | Witcom PP |
| Elastollan® 685 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Karina WHITE PVC COMPOUND -E 830-10/189-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |