Riblene® FC 40
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Riblene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FHUAu4_Riblene-FC-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Riblene FC 40 is a high molecular weight low density polyethylene (LDPE) suitable for blown film extrusion. Riblene FC 40 is characterised by a high melt strength leading to a good bubble stability during extrusion. Films manufactured by Riblene FC 40 are easily heat shrinkable and characterised by high rigidity, good mechanical and excellent optical properties. Main Application Riblene FC 40 is recommended for the production of shrink film for medium and high loads characterized by high rigidity, clarity and gloss. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.928 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.27 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 70 | µm | |
| Film Thickness - Recommended / Available | 40 to 150 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 70 µm, Blown Film | 230 | MPa | |
| 1% Secant, TD : 70 µm, Blown Film | 240 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 70 µm, Blown Film | 12.0 | MPa | |
| TD : Yield, 70 µm, Blown Film | 12.0 | MPa | |
| MD : Break, 70 µm, Blown Film | 28.0 | MPa | |
| TD : Break, 70 µm, Blown Film | 28.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 70 µm, Blown Film | 550 | % | |
| TD : Break, 70 µm, Blown Film | 650 | % | |
| Dart Drop Impact 1(70 µm, Blown Film) | 290 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 70.0 µm | 35.0 | kN/m | |
| TD : 70.0 µm | 50.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 102 | °C | ISO 306/A |
| Melting Temperature | 116 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 70.0 µm, Blown Film) | 70 | ASTM D2457 | |
| Haze (70.0 µm, Blown Film) | 7.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® XT1863-BK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Complet® LCF20-LGF20-PA66 | PlastiComp, Inc. | Nylon 66 | Complet® |
| Fortron® ICE 504L | Celanese Corporation | PPS | Fortron® |
| HAIPLEN H150 T8 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| EPO-TEK® EV2002 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |