SABIC® PPcompound 8620A
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FHIeyo_SABIC-PPcompound-8620A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PPCOMPOUND 8620A is a mineral filled, impact modified polypropylene TPO. It was originally designed for painted automotive bumper fascia applications where a combination of good flow, high stiffness, and cold temperature ductility is required. The IMDS is 209747752. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 21 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 80°C, 1 hr | 0.80 | % | |
| Across Flow : 120°C, 30 min | 0.90 | % | |
| Across Flow : 23°C, 48 hr | 0.70 | % | |
| Flow : 80°C, 1 hr | 0.50 | % | |
| Flow : 120°C, 30 min | 0.60 | % | |
| Flow : 23°C, 48 hr | 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 54 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1900 | MPa | ASTM D638 |
| -- | 1660 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 17.0 | MPa | ASTM D638 |
| Yield | 17.0 | MPa | ISO 527-2/50 |
| Break 3 | 12.0 | MPa | ASTM D638 |
| Break | 13.3 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 4 | 4.7 | % | ASTM D638 |
| Yield | 3.8 | % | ISO 527-2/50 |
| Break 5 | 100 | % | ASTM D638 |
| Break | 41 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1420 | MPa | ASTM D790 |
| 64.0 mm Span 7 | 1780 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 8 | 6.7 | kJ/m² | |
| 0°C 9 | 32 | kJ/m² | |
| 23°C 10 | 55 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C, 3.20 mm 11 | 510 | J/m | ASTM D256 |
| -30°C 12 | 6.6 | kJ/m² | ISO 180/1A |
| 0°C 13 | 31 | kJ/m² | ISO 180/1A |
| 23°C 14 | 48 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact 15(23°C, 3.20 mm) | No Break | ASTM D4812 | |
| Instrumented Dart Impact 16 | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 21.0 | J | |
| 0°C, Energy at Peak Load | 17.6 | J | |
| 23°C, Energy at Peak Load | 16.6 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 99.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 17 | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 53.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 18 | 56.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 122 | °C | ISO 306/A50 |
| Coefficient of Linear Thermal Expansion | ISO 11359-2 | ||
| Flow : -30 to 100°C | 32.6 | µm/Mk | |
| Transverse : -30 to 100°C | 172 | µm/Mk |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 200 to 250 | °C | |
| Front Temperature | 210 to 270 | °C | |
| Nozzle Temperature | 210 to 270 | °C | |
| Processing (Melt) Temp | 210 to 270 | °C | |
| Mold Temperature | 15.0 to 60.0 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4mm, Cut |
| 9 . | 80*10*4 mm, Cut |
| 10 . | 80*10*4 mm, Cut |
| 11 . | 63.5*12.7*3.2mm, Cut |
| 12 . | 80*10*4mm, Cut |
| 13 . | 80*10*4mm, Cut |
| 14 . | 80*10*4mm, Cut |
| 15 . | 63.5*12.7*3.2mm, Cut |
| 16 . | 2.20 m/sec |
| 17 . | 80*10*4mm, Cut |
| 18 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4200 TFE 10 | RTP Company | PI, TP | RTP |
| SLOVAMID® 6 GF 20 FRG 3 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| APICAL 300AV | Kaneka Corporation | Film, PI | APICAL |
| Geon™ Vinyl Rigid Molding M3005 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| HyTemp® AR214 | Zeon Chemicals L.P. | Acrylic, Unspecified | HyTemp® |