LNP™ THERMOCOMP™ KF004A compound
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FGNWqt_LNP-THERMOCOMP-KF004A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* KF004A is a compound based on Acetal Homopolymer resin containing 20% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound KF-1004 D Product reorder name: KF004A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 | % | |
| Across Flow : 24 hr | 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Flexural Modulus | 7100 | MPa | ASTM D790 |
| Flexural Strength | 144 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 430 | J/m | ASTM D4812 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3401-3 | RTP Company | LCP | RTP |
| Sarlink® TPE ML-1240DN | Teknor Apex Company | TPE | Sarlink® TPE |
| Vydyne® 67B | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| ELASTOSIL® LR 3003/50 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| EPAMOULD 786A34 | Epaflex Polyurethanes S.R.L. | TPU-Polyether | EPAMOULD |