Badamid® T70 GF50
| Category: | Nylon 6/6T , Polyamide 6/6T Copolymer |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FGLsLf_Badamid-T70-GF50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% glass fibres reinforced injection moulding grade with superior mechanical properties, high dimensional stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.56 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 3.0 to 4.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.60 to 1.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 18000 | 17000 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Break, 23°C) | 230 | 200 | MPa | ISO 527-2/5 |
| Tensile Strain 2(Break, 23°C) | 2.5 | 2.5 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 15 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 4(23°C) | 85 | 90 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 5 | ||||
| 0.45 MPa, Unannealed | 280 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 275 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 6 | 295 | -- | °C | ISO 3146 |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 145 | -- | °C | |
| some hours | 270 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 7 | 1.0E+13 | -- | ohms | IEC 60093 |
| Volume Resistivity 8 | 1.0E+12 | 1.0E+12 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm 9 | HB | -- | ||
| 1.60 mm 10 | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 310 to 340 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | 80x10x4 mm |
| 4 . | 80x10x4 mm |
| 5 . | 110x10x4 mm |
| 6 . | 10 K/min, Compound for moulding |
| 7 . | 80x80x1 mm |
| 8 . | 80x80x1 mm |
| 9 . | 125x13x0.8 mm |
| 10 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP HR2101D | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| TPX® DX231 | Mitsui Chemicals America, Inc. | PMP Copolymer | TPX® |
| Toraycon® 1494X02 | Toray Resin Company | PBT | Toraycon® |
| NEO-ZEX™ 0134L | Prime Polymer Co., Ltd. | LLDPE | NEO-ZEX™ |
| BJB Polyurethane WC-786 A/B | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |