RTP 2799 S X 118623 B
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FG8LSK_RTP-2799-S-X-118623-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EMI/RFI Shielding |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Moisture Content | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 55 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain, 3.18 mm) | 1.97 | MPa | ASTM D412 |
| Tensile Strength 2(Break, 3.20 mm) | 2.21 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 320 | % | ASTM D412 |
| Tear Strength 4 | 19.3 | kN/m | ASTM D624 |
| Compression Set 5 | ASTM D395B | ||
| 23°C, 22 hr | 12 | % | ASTM D395B |
| 70°C, 22 hr | 64 | % | ASTM D395B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Processing (Melt) Temp | 204 | °C | |
| Mold Temperature | 21.1 - 60.0 | °C |
| Injection instructions |
|---|
| Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps. |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | C mold, 500 mm/min |
| 3 . | Mouth die C, 500 mm/min |
| 4 . | C mould |
| 5 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA66G15-BK10 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| RTP 4005.3 FR A HS | RTP Company | PPA | RTP |
| UBESTA P3014 U | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| DynaPath™ 3168 CF | Polymer Dynamix | PEI | DynaPath™ |
| TOTAL Polystyrene Compound 260-50 | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |