Braskem PE SEB853/72
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem America Inc. |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FFpXsI_Braskem-PE-SEB853-72.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: SEB853/72 is a grade produced under high pressure technology. Films obtained with this product show outstanding optical properties, good sealability, and low gel amount. The minimum biobased content of this grade is 95%, determined according to ASTM D6866. Additives: Slip Agent Medium. Antiblocking Agent Medium. Applications: Lamination film; general purpose; automatic packaging of solids products (FFS). Process: Blown Film Extrusion. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.7 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 30.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 20.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 270 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 1000 | % | ASTM D882 |
| Dart Drop Impact 1(38 µm, Blown Film) | 70 | g | ASTM D1709 |
| Elmendorf Tear Strength - TD (38 µm, Blown Film) | 100 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60 °, blown film) | 112 | ASTM D2457 | |
| Haze (Blown Film) | 5.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 95 | % | ASTM D6866 |
| Blown Film Properties: 38µm thickness film, processed in a 75 mm screw diameter extruder with blow up ratio of 2:1, die gap 1.0 mmRecommended process conditions:Blown Film ExtrusionExtruder:Screw- relation L/D..........16 to 30:1Compression Ratio.........3 to 4:1Screw Package (Mesh)...40/60/40Temperature Profile: 1st zone............................110°C Extruder..........................150°C Die..................................160°C Blow up ratio...................from 2 to 3:1Frostline Height...............maximum equivalent to bubble diameter |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHLEN M9451D | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| THERMOLAST® K TC6SCE (Series: SCR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Evermore PUR UP-9460NHR | Evermore Chemical Industry Co., Ltd. | PUR-Ether | Evermore PUR |
| K-Prene D 6077 (Type A) | Technovinyl Polymers India Ltd. | SBS | K-Prene |
| PEARLSTICK® 45-40/15 | Lubrizol Advanced Materials, Inc. | TPU-Capro | PEARLSTICK® |