KOPPS® S23G40BL
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPPS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FF86i3_KOPPSS23G40BL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KOPPS®S23G40BL is a polyphenylene sulfide (PPS) product, which contains a 40% glass fiber reinforced material. It is available in North America, Latin America, Europe or Asia Pacific. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.1 | % | ISO 294-4 |
| Flow | 0.25 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 175 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.8 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 14500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 265 | °C | ISO 75-2/A |
| Melting Temperature | 285 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 160 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 120 - 130 | °C | |
| Drying Time - Desiccant Dryer | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 290 - 310 | °C | |
| Front Temperature | 290 - 310 | °C | |
| Nozzle Temperature | 300 - 320 | °C | |
| Mold Temperature | 120 - 140 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tectron H2273 | TECTRON Systems Pte Ltd | TPV | Tectron |
| T-Blend® 0092N-NE | TSRC Corporation | SEBS | T-Blend® |
| Amilan® CM1046K4 | Toray Resin Company | Nylon 6 | Amilan® |
| CAPROWAX P鈩?6006-00-000 Pulver | POLYFEA | Biodeg Polymers | CAPROWAX P™ |
| Desmopan® DP 1050D | Covestro - PUR | TPU, Unspecified | Desmopan® |