SLOVAMID® 6 GF 30 FRG 2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Plastcom |
| Trademark: | SLOVAMID® 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FEpu0k_SLOVAMID-6-GF-30-FRG-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| With 30% glass fiber reinforced PA 6 for chemical injection molding has increased strength and toughness. Use in the production of structural parts in the automotive, electronics, machinery and consumer goods industry - eg Holders of electrical hand tools, hobby equipment, housing the electric equipment, gears, propellers for fans, electric motors. The halogen-free product is supplied in natural form or in the colors of the RAL scale. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 0.58 | % | |
| Flow | 0.46 | % | |
| Water Content | 0.15 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 165 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 8540 | MPa | ISO 178 |
| Flexural Stress | 225 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 8.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 46 | kJ/m² | |
| 23°C | 68 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 215 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 225 | °C | ISO 306/B |
| Melting Temperature (DSC) | 225 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | 70 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 3.20 mm | V-2 | ||
| 1.60 mm | V-1 | ||
| 0.800 mm | V-0 | ||
| Glow Wire Ignition Temperature | 850 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Pressure | 70.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRESEAL® TPE 6080 | Premix Oy | TPE | PRESEAL® |
| 3M™ Dyneon™ PTFE Compound TF 3311 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| GAPEX® HP RPP30EU92BK | Ferro Corporation | PP, Unspecified | GAPEX® HP |
| LAMINEX® 2010 | Schwartz Technical Plastic | PF | LAMINEX® |
| Pinnacle PP 3220 | Pinnacle Polymers | PP Impact Copolymer | Pinnacle PP |