Sumitomo Epoxy EM 7302LD-2
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Sumitomo Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FDrp1Z_Sumitomo-Epoxy-EM-7302LD-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EM 7302LD-2 is a long fiberglass reinforced epoxy molding compound with a low density inert filler. This compound is designed for applications where moderate strength and weight savings are desirable. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 to 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (Compression Molded) | 0.14 | % | ASTM D955 |
| Water Absorption - 48 hr (50°C) | 0.29 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 76.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 17200 | MPa | ASTM D790 |
| Flexural Strength (Break) | 213 | MPa | ASTM D790 |
| Compressive Strength | 190 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 1200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, Compression Molded) | > 280 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 9.3 | kV/mm | ASTM D149 |
| Dielectric Constant 1(1 MHz) | 2.80 | ASTM D2520 | |
| Dissipation Factor 2(1 MHz) | 0.017 | ASTM D150 | |
| Arc Resistance | 120 | sec | ASTM D495 |
| Note Message | |
|---|---|
| 1 . | Wet |
| 2 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HMN 5445 | Saudi Polymers Company | HDPE | Marlex® |
| ARCEL® LD (3.00 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| OmniLon™ PA6/6 IM4 FR0 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| LNP™ THERMOCOMP™ IF006L compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |
| CERTENE™ 1320 | Muehlstein | PS (HIPS) | CERTENE™ |