GLAMIDE® T-403
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FDr8Lh_GLAMIDE-T-403.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GLAMIDE® T-403 is a Polyamide 6 (Nylon 6) product filled with 45% glass fiber. It is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.48 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 4.0 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.10 to 0.30 | -- | % | |
| 3.00 mm | 0.30 to 0.60 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.1 | -- | % | |
| Equilibrium, 65% RH | 1.9 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 290 | 250 | MPa | |
| Yield, 23°C | 200 | 130 | MPa | |
| Yield, 80°C | 120 | 90.0 | MPa | |
| Tensile Elongation (Break, 23°C) | 3.2 | 3.4 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 13900 | 12500 | MPa | |
| 23°C | 12000 | 7200 | MPa | |
| 80°C | 6800 | 4500 | MPa | |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 360 | 300 | MPa | |
| Yield, 23°C | 290 | 180 | MPa | |
| Yield, 80°C | 150 | 100 | MPa | |
| Compressive Strength (23°C) | 160 | -- | MPa | ASTM D695 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 120 | 140 | J/m | |
| 23°C | 190 | 250 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 217 | -- | °C | |
| 1.8 MPa, Unannealed | 217 | -- | °C | |
| CLTE - Flow | 2.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 25 | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 4.20 | -- | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.010 | -- | ASTM D150 | |
| Arc Resistance | 100 | 92.0 | sec | ASTM D495 |
| Comparative Tracking Index | 550 | 550 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Pressure | 75.0 to 95.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Appeel® 72D727 | DuPont Packaging & Industrial Polymers | EVA | Appeel® |
| Ecomass® 2150TU96 | Ecomass Technologies | Nylon 66 | Ecomass® |
| Karina CLEAR PVC COMPOUND -E 80/235-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ IFL34 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ LUBRICOMP™ |
| Polychim HC10XC | Polychim Industrie S.A.S. | PP Homopolymer | Polychim |