FERREX® GPP40CC90UL
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | FERREX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FCs982_FERREX-GPP40CC90UL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FERREX®GPP40CC90UL is a polypropylene homopolymer (PP Homopoly) material, and its filler is 40% calcium carbonate filler. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. FERREX®The main features of the GPP40CC90UL are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.3 | % | ASTM D955 |
| Transverse flow | 1.6 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 24.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 35 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 2100 | MPa | ASTM D790 |
| Tangent : 23°C | 2410 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 43.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D256 |
| Dart Drop Impact | 18.6 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 116 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 65.6 | °C | ASTM D648 |
| Additional Information |
|---|
| Filler Content, ASTM D2584: 40% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL8F 801 | Marco Polo International, Inc. | LLDPE | MARPOL® |
| Taitacell EPS 301S | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| THERMOLAST® K TC8CSN (Series: CS) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Akulon® Ultraflow K-FPG8 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| Geon™ Vinyl Rigid Extrusion LR620 white 1046 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |