Polytron® P30B03
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | Polytron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FCkV5h_Polytron-P30B03.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A Chemically Coupled 30% Long Glass Fiber Reinforced Black Polypropylene, Heat Stabilized for Injection Moulding application. These products have significantly improved impact performance characteristics compared to other grades of Polyproplene long fiber thermoplastics. The room temperature Charpy impact properties are 25 to 30% higher at room temperature and at low temperature (-40°C). The material is supplied in Pellets that are typically 11-13mm in length. Fiber length is the length of the Pellets. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.10 to 0.20 | % | ASTM D955 |
| -- | 0.10 to 0.20 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6250 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 85.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 6100 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 130 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 14 | kJ/m² | |
| 23°C | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 75 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D256 |
| -30°C | 17 | kJ/m² | ISO 180 |
| 23°C | 16 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 149 | °C | ASTM D648, ISO 75-2/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Flammability (2.00 mm) | 10 | mm/min | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ LLDPE 1613.11 | The Dow Chemical Company | LLDPE | DOW™ LLDPE |
| Delrin® 127UV BK701 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| ExxonMobil™ PP8013L1 | ExxonMobil Chemical | PP Impact Copolymer | ExxonMobil™ |
| Latene® 7-V2 | LATI S.p.A. | PP Homopolymer | Latene® |
| Sylvin 4200-60 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |