Bergamid™ X2 B70 U NC
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | FCZYUi_Bergamid-X2-B70-U-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Bergamid™ X2 B70 U NC is a Polyamide 6 (Nylon 6) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, or Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1(23°C) | 1.27 | g/cm³ | DIN 53479 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm) | 3800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C, 4.00 mm) | 77.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C, 4.00 mm) | 3.2 | % | ISO 527-2/50 |
| Flexural Modulus (23°C) | 2900 | MPa | ISO 178 |
| Flexural Stress (23°C) | 98.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.6 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 223 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 275 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.400 mm | V-2 | ||
| 0.800 mm, ALL | V-2 | ||
| 1.60 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 960 | °C | |
| 1.60 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.400 mm | > 825 | °C | |
| 0.800 mm | 825 | °C | |
| 1.60 mm | 825 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | ±0.03 g/cm³ |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ratron® 250C6 | Asia International Enterprise (Hong Kong) Limited | PESU | Ratron® |
| Moplen RP218R | LyondellBasell Industries | PP Random Copolymer | Moplen |
| Texin® 1209 | Covestro - PUR | TPU-Polyether | Texin® |
| UBE Nylon 5034 MTAX1 | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| ULTEM™ 1010P resin | SABIC Innovative Plastics | PEI | ULTEM™ |