ACRYLITE® Resist ZK5BR

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Cyro LLC
Trademark:	ACRYLITE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	FCVAci_ACRYLITE-Resist-ZK5BR.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

ACRYLITE® Resist ZK5BR polymer is an amorphous, impact-modified thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA).

Typical properties of ACRYLITE® Resist acrylic polymers are:

high weather resistance

high light transmission

improved resistance to stress cracking

good melt flow rate

easy to color

The special properties of ACRYLITE® Resist ZK5BR polymer are:

medium impact/break resistance and strength

brilliant optical clarity

low melt flow rate

high heat resistance

AMECA listed

Application:
Used for injection molded parts.

General Information
Additive	Impact Modifier
Features	Amorphous Good Colorability Good Impact Resistance Good Strength Good Weather Resistance High Clarity High Heat Resistance Impact Modified Low Flow Opticals
Uses	Appliance Components Decorative Displays Household Goods Housings Lenses Lighting Applications
Agency Ratings	EC 1907/2006 (REACH)
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.18	g/cm³	ASTM D792
Apparent Density	0.71	g/cm³	ASTM D1895
Melt Mass-Flow Rate (MFR) (230°C/3.8 kg)	3.4	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.40 to 0.70	%	ASTM D955
Water Absorption (Equilibrium)	< 0.30	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	70		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2480	MPa	ASTM D638
Tensile Strength	62.1	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	5.0	%
Break	30	%
Flexural Modulus	2280	MPa	ASTM D790
Flexural Strength	88.9	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
0°C, 6.35 mm	27	J/m
23°C, 6.35 mm	43	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)	98.9	°C	ASTM D648
Vicat Softening Temperature	103	°C	ASTM D1525
CLTE - Flow (0 to 100°C)	7.2E-5	cm/cm/°C	ASTM D696

Optical	Nominal Value	Unit	Test Method
Transmittance (3200 µm)	> 90.0	%	ASTM D1003
Haze (3200 µm)	< 2.0	%	ASTM D1003
Yellowness Index (3.20 mm)	0.30	YI	ASTM D1925

Resin Grade	Manufacturer	Category	Trademark
China PPS PTFE-hGR312	Sichuan Deyang Chemical Co., Ltd	PPS	China PPS
Comtrex Flexible PVC® 71XCF	Mitsubishi Chemical Performance Polymers, Inc.	PVC, Flexible	Comtrex Flexible PVC®
GPPC ABS D-1200	GPPC Chemical Co., Ltd.	ABS	GPPC ABS
HYDEL® PEI-7	Ensinger Inc.	PEI	HYDEL®
RONFALIN® ABS 1541	A. Schulman Europe	ABS	RONFALIN®