ISPLEN® PP 040 G1E

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	REPSOL
Trademark:	ISPLEN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	FAQgGh_ISPLEN-PP-040-G1E.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
ISPLEN® PP 040 G1E is a medium-low melt flow rate polypropylene homopolymer. It offers a good balance between mechanical and processing properties for production of tapes. It is formulated with an additive package suitable for protecting the polymer during extrusion process and final use. TYPICAL APPLICATIONS Low fibrillation tapes for textil uses Monofilaments and tapes for ropes and twines Sheet extrusion and thermoforming Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line.

Message

ISPLEN® PP 040 G1E is a medium-low melt flow rate polypropylene homopolymer. It offers a good balance between mechanical and processing properties for production of tapes. It is formulated with an additive package suitable for protecting the polymer during extrusion process and final use.

TYPICAL APPLICATIONS

Low fibrillation tapes for textil uses

Monofilaments and tapes for ropes and twines

Sheet extrusion and thermoforming

Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line.

General Information
Additive	Processing Stabilizer
Features	Food Contact Acceptable Medium Flow
Uses	Monofilaments Rope Sheet Tape Twine
Agency Ratings	EU Food Contact, Unspecified Rating
Processing Method	Filament Extrusion Sheet Extrusion Thermoforming

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	3.0	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	35.0	MPa	ISO 527-2
Flexural Modulus	1350	MPa	ISO 178

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (0.45 MPa, Unannealed)	91.0	°C	ISO 75-2/B
Vicat Softening Temperature	153	°C	ISO 306/A

Extrusion	Nominal Value	Unit
Melt Temperature	190 to 250	°C

Resin Grade	Manufacturer	Category	Trademark
AT 7110	Celanese EVA Performance Polymers	LDPE	AT
GAPEX® RPP30EU55HB BLACK	Ferro Corporation	PP Copolymer	GAPEX®
Horda E8201	Horda Cable Compounds	PE, Unspecified	Horda
JSR EPR T7141	JSR Corporation	EPDM	JSR EPR
OmniLon™ PA6/6 U GR25 BK1000	OMNI Plastics, LLC	Nylon 66	OmniLon™