LNP™ THERMOCOMP™ BF006 compound
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F9AqgL_LNP-THERMOCOMP-BF006-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP BF006 is a compound based on Styrene Acrylonitrile resin containing Glass Fiber. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.14 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 91.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7800 | MPa | ISO 178 |
| Flexural Stress | 109 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 108 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 103 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.6E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.8E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE ML-1240D BLK 111 | Teknor Apex Company | TPE | Sarlink® TPE |
| SPI HOPP12 | Service Polymers, Inc. | PP Homopolymer | SPI |
| Axiall PVC 1702 Clear 7070 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| LUVOCOM® 1104-8928 | Lehmann & Voss & Co. | PEK | LUVOCOM® |
| ESTOPLAST EP 4130RD05 | Ester Industries Ltd. | PBT | ESTOPLAST EP |