LNP THERMOCOMP UFW49RSC is a compound based on Polyphthalamide resin containing Glass Fiber, Mineral. Added features include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound UFM-3249 HS-S VDO Product reorder name: UFW49RSC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.87 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 20800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 186 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 1.1 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 18100 | MPa | ISO 178 |
| Flexural Stress | 278 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 255 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.6E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 3.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 to 321 | °C | |
| Middle Temperature | 316 to 327 | °C | |
| Front Temperature | 327 to 338 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Auracell® MH | Rotuba Extruders, Inc. | CA | Auracell® |
| Devcon HP 250 | Devcon | Epoxy | Devcon |
| Geon™ Vinyl Flexible H41276D | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Ensinger TECACRYL® | Ensinger Inc. | Acrylic, Unspecified | Ensinger |
| Petrotene® PP A3 C35 BRC0001 PH383 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |