SABIC® PPcompound 7175U
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F8VNHv_SABICPPcompound7175U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 7175U is an elastomer-modified mineral filled Polypropylene for automotive exterior applications. The material is UV stabilized. SABIC® PPcompound 7175U is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.90 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20mm, injection molding | 19.5 | MPa | ISO 527-2/5/50 |
| Fracture, 3.20mm, injection molding | 13.5 | MPa | ISO 527-2/5/50 |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 80 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1400 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/4A | ||
| -20°C, injection molding | 5.5 | kJ/m² | ISO 180/4A |
| 0°C, injection molding | 50 | kJ/m² | ISO 180/4A |
| 23°C, injection molding | 60 | kJ/m² | ISO 180/4A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 100 | °C | ISO 75-2/B |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 7.5E-5 | cm/cm/°C | ASTM D696 |
| 23 to 80°C | 9.5E-5 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Method I (three-point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® M | Röchling Engineering Plastics SE & Co. KG | UHMWPE | POLYSTONE® |
| Sicoflex S299 | Ravago Group | ABS | Sicoflex |
| VITAMIDE® AY24BK6722 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| LGSTRENE LGG 101 | LG Polymers India Pvt. Ltd. | PS (GPPS) | LGSTRENE |
| Panlite® G-3430R | TEIJIN LIMITED | PC | Panlite® |