MELMEX M Fine
| Category: | Mel Formald , Melamine Formaldehyde |
| Manufacturer: | BIP (Oldbury) Limited |
| Trademark: | MELMEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F8PBB5_MELMEX-M-Fine.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A fine powder normally pelleted and HF Preheated to give superior surface finish for such articles as tableware and ashtrays. Available in a wide range of colours. Suitable for food contact applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ISO 1183 |
| Apparent Density | 0.44 | g/cm³ | ISO 60 |
| Bulk Factor | 3.5 | ISO 171 | |
| Molding Shrinkage | ISO 2577 | ||
| -- 1 | 0.58 | % | |
| -- 2 | 0.62 | % | |
| Water Absorption | |||
| Cold 3 | 70.0 | mg | DIN 53472 |
| Cold 4 | 13.0 | mg | ISO 62 |
| Hot 5 | 50.0 | mg | ISO 62 |
| Post Shrinkage | ISO 2577 | ||
| -- 6 | 0.85 | % | |
| -- 7 | 1.1 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Martens Temperature | 145 | °C | DIN 43458 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Stress | 119 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 2.2 | kJ/m² | ISO 180/C |
| Unnotched Izod Impact Strength | 9.8 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 186 | °C | ISO 75-2/Ae |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | IEC 60243-1 | ||
| -- 8 | 8.5 | kV/mm | |
| -- 9 | 6.1 | kV/mm | |
| Comparative Tracking Index | > 600 | V | IEC 60167 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 | |
| Oxygen Index 10 | 44 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Preheated powder |
| 2 . | Cold powder |
| 3 . | 96 hr @ 23°C |
| 4 . | 24 hr @ 23°C |
| 5 . | 30 min @ 100°C |
| 6 . | Cold powder |
| 7 . | (48 hr) Preheated powder |
| 8 . | (90°C) Preheated powder |
| 9 . | Cold powder |
| 10 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene G13P100-559UV | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Stanyl® 46HF5041LW | DSM Engineering Plastics | Nylon 46 | Stanyl® |
| Sympoxy™ 1871 | Hapco Inc. | Epoxy | Sympoxy™ |
| ELASTOSIL® M 4644 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® M |
| XENOY™ CL100 resin | SABIC Innovative Plastics Europe | PC+PBT | XENOY™ |