AvaSpire® AV-651 GF30
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | AvaSpire® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F8K9Ih_AvaSpire-AV-651-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AvaSpire® AV-651 GF30 is a 30% glass fiber reinforced polyaryletherketone (PAEK) that has been specifically formulated to provide higher mechanical strength and stiffness than unfilled AV-651 resin. This resin offers chemical resistance nearly equivalent to glass fiber-reinforced PEEK in most chemicals, with a lower heat deflection temperature. These properties make it well suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses.
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow : 3.18 mm | 0.20 to 0.40 | % | |
| Across Flow : 3.18 mm | 1.3 to 1.5 | % | |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 101 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 9900 | MPa | ASTM D638 |
| -- | 10400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | |||
| Yield, 5.00 mm | 162 | MPa | ISO 527-2/1A/5 |
| -- 3 | 156 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break 4 | 2.9 | % | ASTM D638 |
| Break | 2.9 | % | ISO 527-2/1A/5 |
| Flexural Modulus | |||
| -- | 9400 | MPa | ASTM D790 |
| -- | 9700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 234 | MPa | ASTM D790 |
| -- | 228 | MPa | ISO 178 |
| Compressive Strength | 168 | MPa | ASTM D695 |
| Shear Strength | 82.6 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 110 | J/m | ASTM D256 |
| -- | 12 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| -- | 960 | J/m | ASTM D4812 |
| -- | 64 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 213 | °C | ASTM D648 |
| Glass Transition Temperature | 158 | °C | ASTM D3418 |
| Peak Melting Temperature | 345 | °C | ASTM D3418 |
| CLTE - Flow (-50 to 50°C) | 1.7E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | DSC | ||
| 50°C | 1270 | J/kg/°C | |
| 200°C | 1650 | J/kg/°C | |
| Thermal Conductivity | 0.30 | W/m/K | ASTM E1530 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.9E+17 | ohms | ASTM D257 |
| Volume Resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.61 | ||
| 1 kHz | 3.63 | ||
| 1 MHz | 3.58 | ||
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 2.0E-3 | ||
| 1 kHz | 0.0 | ||
| 1 MHz | 4.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-1 | ||
| 1.60 mm | V-0 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C, 1000 sec^-1) | 410 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 365 | °C | |
| Middle Temperature | 371 | °C | |
| Front Temperature | 377 | °C | |
| Nozzle Temperature | 382 | °C | |
| Processing (Melt) Temp | 366 to 388 | °C | |
| Mold Temperature | 160 to 190 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 5" x 0.5" x 0.125" bars |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC A3 HF UV VRD0278 PC303 | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| Axiall PVC 8573 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Evatane® 24-03 | Arkema | EVA | Evatane® |
| Fainplast PVC CKL 76/V | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| HANWHA LDPE 737 | Hanwha Chemical | LDPE | HANWHA LDPE |