INEOS LLDPE LL6120AA
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F6dXGk_INEOS-LLDPE-LL6120AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LL6120AA is particularly suitable for high performance cast stretch film applications and can be used, for example, as a core layer in co-extruded structures. This grade is also recommended for artificial grass applications. Characteristics LL6120AA is a linear low density polyethylene copolymer containing hexene (C6) as the comonomer. It offers the following properties:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Modulus | ISO 527-3/150 | ||
| 1% Secant, MD : 20 µm | 100 | MPa | |
| 1% Secant, TD : 20 µm | 120 | MPa | |
| Tensile Strength | ISO 527-3/150 | ||
| MD : 20 µm | 33.0 | MPa | |
| TD : 20 µm | 25.0 | MPa | |
| Tensile Elongation | ISO 527-3/150 | ||
| MD : Break, 20 µm | 600 | % | |
| TD : Break, 20 µm | 750 | % | |
| Dart Drop Impact (20 µm) | 180 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20.0 µm | 98.1 | kN/m | |
| TD : 20.0 µm | 227.5 | kN/m |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance | 350000 | J/m | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm) | 93 | ASTM D2457 | |
| Haze (20.0 µm) | 1.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 240 to 280 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC5-2010 | Spartech Polycom | PP Copolymer | Spartech |
| SuperKleen 3003-85 CLEAR 0003 | AlphaGary | PVC, Flexible | SuperKleen |
| Nordbak High Performance Backing | Loctite® | Epoxy | Nordbak |
| Hifax ETA4161UV | LyondellBasell Industries | TPO (POE) | Hifax |
| LNP™ LUBRICOMP™ UCL36S compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |