Vyncolit® X655RB
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F6LlQM_Vyncolit-X655RB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® X655RB is a glass fiber and mineral filled phenolic molding compound with superior stiffness, high dimensional stability and high wear resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.08 | g/cm³ | ISO 1183 |
| Apparent Density | 1.04 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.15 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ISO 62 |
| Post Shrinkage | 0.020 | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 0.75 | % | ISO 178 |
| Tensile Modulus | 30000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.45 | % | ISO 527-2 |
| Flexural Modulus | 25000 | MPa | ISO 178 |
| Flexural Stress | 190 | MPa | ISO 178 |
| Compressive Stress | 360 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.7 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 8.7 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 223 | °C | ISO 75-2/Af |
| CLTE | TMA | ||
| Flow | 1.2E-5 | cm/cm/°C | |
| Transverse | 2.2E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.7E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 325 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers SBS 1003 | Network Polymers, Inc. | SBS | Network Polymers SBS |
| Daelim Po1y® PP-141 | DAELIM INDUSTRIAL CO., LTD. | PP, Unspecified | Daelim Po1y® |
| Fainplast PVC FKT 92 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Geon™ Vinyl Flexible XV3861 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LUVOCOM® 20-0791 | Lehmann & Voss & Co. | PPA | LUVOCOM® |