Sarlink® TPV 24809
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F5wcFa_Sarlink-TPV-24809.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sarlink 24809 is a very low durometer thermoplastic vulcanizate designed for indstrial applications requiring UV resistance. Sarlink 24809 is suitable for injection molding and extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.890 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 14 | ASTM D2240 | |
| Shaw A, 5 seconds | 10 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain 1 | 0.303 | MPa | ASTM D412 |
| Flow : 100% strain 2 | 0.359 | MPa | ASTM D412 |
| Transverse flow : 300% strain 3 | 0.889 | MPa | ASTM D412 |
| Flow : 300% strain 4 | 0.824 | MPa | ASTM D412 |
| Tensile Strength 5 | ASTM D412 | ||
| Transverse flow : Fracture | 1.04 | MPa | ASTM D412 |
| Flow : Fracture | 0.945 | MPa | ASTM D412 |
| Tensile Elongation 6 | ASTM D412 | ||
| Transverse flow : Fracture | 340 | % | ASTM D412 |
| Flow : Fracture | 310 | % | ASTM D412 |
| Tear Strength 7 | ASTM D624 | ||
| Transverse flow | 3.68 | kN/m | ASTM D624 |
| Flow | 4.20 | kN/m | ASTM D624 |
| Compression Set 8 | ASTM D395B | ||
| 23°C, 22 hr | 10 | % | ASTM D395B |
| 70°C, 22 hr | 24 | % | ASTM D395B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 149 - 182 | °C | |
| Middle Temperature | 160 - 182 | °C | |
| Front Temperature | 166 - 188 | °C | |
| Nozzle Temperature | 177 - 204 | °C | |
| Processing (Melt) Temp | 177 - 204 | °C | |
| Mold Temperature | 26.7 - 48.9 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 40 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 143 - 166 | °C | |
| Cylinder Zone 2 Temp. | 149 - 171 | °C | |
| Cylinder Zone 3 Temp. | 154 - 177 | °C | |
| Cylinder Zone 5 Temp. | 154 - 182 | °C | |
| Die Temperature | 154 - 177 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | Mouth die C, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | C mold, 510mm/min |
| 6 . | Mouth die C, 510mm/min |
| 7 . | C mold, 510mm/min |
| 8 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultrathene® UE624000 | LyondellBasell Industries | EVA | Ultrathene® |
| AMTOPP CI25 | Inteplast Group | PP, Unspecified | AMTOPP |
| Ferro PP LPP30BD16BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| INSPIRE™ T710-25 ES | Trinseo | PP, Unspecified | INSPIRE™ |
| K-Bin Rigid PVC KB-5006 | K-Bin, Inc. | PVC, Rigid | K-Bin Rigid PVC |