AKROMID® A3 GM 20/10 S1 natural (1217)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F5A7eA_AKROMID-A3-GM-20-10-S1-natural-1217-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GM 20/10 S1 natural (1217) is an 20% glass fibre reinforced, 10% glass bead filled, cold impact strength polyamide 6.6 with good surface, low warpage and light inherent color Applications are technical devices in automotive and engineering industry capable of carrying high load. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.31 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.3 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption (Saturation, 23°C) | 5.1 | -- | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 2.0 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 30 | -- | % | ISO 1172 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 127 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6900 | 4200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 130 | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.0 | 10 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 6900 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 205 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 8.0 | -- | kJ/m² | |
| 23°C | 15 | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 76 | -- | kJ/m² | |
| 23°C | 80 | 80 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 245 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 262 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zythane® 4060A | Alliance Polymers & Services | TPU-Polyester | Zythane® |
| Cheng Yu SW10 | Cheng Yu Plastic Company Limited | Acetal (POM) Copolymer | Cheng Yu |
| Durethan® BG 30 X FN01 000000 | LANXESS GmbH | Nylon 6 | Durethan® |
| Karina IVORY PVC COMPOUND -E 800-35/ 1-B-ERB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLIMAXX 1175SM | IRPC Public Company Limited | PP Homopolymer | POLIMAXX |