Bergamid™ A70 G30 TF15 H MOS2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F4mew2_BergamidA70G30TF15HMOS2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber Reinforced PA66 Compound with Heat resistant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.49 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 0.30 - 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 10000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C, 4.00 mm, Injection Molded) | 160 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C, 4.00 mm, Injection Molded) | 3.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C, Injection Molded) | 9.0 | kJ/m² | ISO 179 |
| Unnotched Izod Impact Strength (23°C, Injection Molded) | 80 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 245 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.6 mm) | HB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 240 - 280 | °C | |
| Middle Temperature | 240 - 280 | °C | |
| Front Temperature | 240 - 280 | °C | |
| Mold Temperature | 65 - 85 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | bergmann method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PP H105-03NA | Braskem Europe GmbH | PP Homopolymer | Braskem PP |
| Elastollan® C 60 A HPM | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| INSTRUC TPUGF30 70D | Infinity LTL Engineered Compounds | TPU, Unspecified | INSTRUC |
| Innothane® IE-3010 | Innovative Polymers, Inc. | TSU | Innothane® |
| Sylvin 5145-70 Red 6193 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |