Pro-fax SB912
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Pro-fax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F4FLc1_Pro-fax-SB912.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pro-fax SB912 fully formulated impact polypropylene copolymer is available in pellet form. This resin is typically used in injection molding applications and offers homopolymer-like stiffness. For regulatory compliance information see Pro-fax SB912 Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792B |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 32.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 8.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 2 | 1520 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 75 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 113 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® 1021ST BRIGHT | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |
| Spartech Polycom SC7-7010F | Spartech Polycom | PC | Spartech |
| SUPREME GPPS SC 202EL | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| DuraGrip® DGR 6040NC | Advanced Polymer Alloys | TPE | DuraGrip® |
| TOTAL Polystyrene Crystal 1050T | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |