Hostalen CRP 100 black (XL)
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F1yxpC_Hostalen-CRP-100-black-XL-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen CRP 100 black (XL) is a high density polyethylene (HDPE), black coloured similar RAL 9004 with high melt viscosity and higher zero viscosity. Typical application: Extrusion of extra large and thick walled pipes to avoid the sagging. The product is classified as PE 100 and provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength. It is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.959 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.23 | g/10 min | |
| 190°C/21.6 kg | 6.4 | g/10 min | |
| Carbon Black Content | 2.3 | % | ISO 6964 |
| FNCT (80°C) 1 | > 1.4 | month | ISO 16770 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Creep Modulus 2 | DIN 19537-2 | ||
| 1 min | 1.20 | GPa | |
| 2000 hr | 0.330 | GPa | |
| 24 hr | 0.560 | GPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (210°C) | 30 | min | ISO 11357-6 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MRS Classification | 10.0 | MPa | ISO TR 9080 |
| Odor Threshold | < 2.00 | EN 1622/EN 1420 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 8.0 | % | ISO 527-2/50 |
| Tensile Creep Modulus 3 | ISO 899-1 | ||
| 1 hr | 850 | MPa | |
| 1000 hr | 360 | MPa |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation (Break) | > 350 | % | EN 638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 26 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 74.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 to 220 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 4.0 MPa, 2% Arkopal N 100 |
| 2 . | 4 point loading method |
| 3 . | 2.0 MPa load |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trademark PE HD10950 | Trademark Plastics Corporation | HDPE | Trademark PE |
| Chemical Resources GPPS600 | Chemical Resources, Inc. | PS (GPPS) | Chemical Resources |
| KW Plastics KWR105M2-7625 | KW Plastics | HDPE | KW Plastics |
| LNP™ THERMOCOMP™ AW00A compound | SABIC Innovative Plastics Europe | ABS | LNP™ THERMOCOMP™ |
| Sumiliteresin® PR-1303 I | SBHPP | Phenolic | Sumiliteresin® |