INEOS Wire & Cable BPD8128
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS Wire & Cable |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | F1ePVT_INEOS-Wire-Cable-BPD8128.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BPD 8128 is a high molecular weight low density polyethylene compound specially designed for crosslinking with silanes. It is a "non staining" Monosil® product that contains a controlled amount of metal-deactivator and antioxidant to provide the desired copper contact performance. BPD 8128 is widely used by cable manufacturers using a Silane® (one step) crosslinking process. Its major area of application is for the insulation of low voltage power cables. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.27 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 15.0 | MPa | IEC 60811-1-1 |
| Tensile Strain (Break) | 350 | % | IEC 60811-1-1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 168 hr) | < 25 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Constant (50 Hz) | < 2.35 | ASTM D150 | |
| Dissipation Factor (50 Hz) | < 3.0E-3 | ASTM D150 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Elongation 1(200°C) | 50 | % | IEC 60811-2-1 |
| All the tests have been performed on cables extruded on a Nokia Maillefer BMA 45 30L/D monosil line with 1.5% of a commercial mixture of vinyl trimethoxysilane, peroxide, crosslinking catalyst (ex: SILCAT R) and a suitable package of antioxidants. The cables have been crosslinked 4h in water at 80°C. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 140 | °C | |
| Cylinder Zone 2 Temp. | 150 | °C | |
| Cylinder Zone 3 Temp. | 160 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Cylinder Zone 5 Temp. | 190 | °C | |
| Melt Temperature | 220 - 230 | °C | |
| Die Temperature | 220 | °C |
| Extrusion instructions |
|---|
| Zone 6 Temperature: 200°CZone 7 Temperature: 210°CHead Temperatures: 210-220-220°CScrew Cooling: 80°C |
| Note Message | |
|---|---|
| 1 . | 15 min, 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STAR-THERM® E B-2C | EPIC Polymers | Nylon 6 | STAR-THERM® |
| NORYL™ 6390H resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |
| Lucobit 1235 | Lucobit AG | PE Copolymer | Lucobit |
| INEOS PP 102-GF02 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |
| CYCOLAC™ INP581 resin | SABIC Innovative Plastics | ABS+SAN | CYCOLAC™ |