LEXAN™ LGK4030 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EzVrHc_LEXAN-LGK4030-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN™ LGK4030 resin is a Polycarbonate (PC) material. It is available in Asia Pacific. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.54 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.15 to 0.20 | % | Internal Method |
| Water Absorption (24 hr) | 0.14 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 91 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 129 | MPa | Internal Method |
| Tensile Elongation (Break) | 3.0 to 5.0 | % | Internal Method |
| Flexural Modulus | 8820 | MPa | ASTM D790 |
| Flexural Strength | 180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 145 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 2.2E-5 to 4.3E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1405 B | RTP Company | PESU | RTP |
| ADENE OCYBG | A.D. Compound spa | PP Copolymer | ADENE |
| Pinnacle PP 4211 | Pinnacle Polymers | PP Impact Copolymer | Pinnacle PP |
| Moplen EP5079 | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| CYCOLOY™ MC1300 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |