Order Products : sales@su-jiao.com
Clyrell RC354N
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Clyrell |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EyfkPI_Clyrell-RC354N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Clyrell RC354N is a random copolymer suitable for extrusion applications. It is formulated with an anti-gasfading stabilisation package. Clyrell RC354N is designed for the production of fine denier staple fibres with enhanced softness. It is used either pure or in blend with PP homopolymer. Typical application is thermal-bonded nonwovens. For regulatory information please refer to Moplen RC354N Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 10 | % | |
| Break | > 50 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 68.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 129 | °C | ISO 306/A50 |
| -- | 68.0 | °C | ISO 306/B50 |
| Melting Temperature | 141 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205.3 TFE 5 | RTP Company | Nylon 66 | RTP |
| SLOVAMID® 6 GF 60 000/1M | Plastcom | Nylon 6 | SLOVAMID® 6 |
| NatureFlex™ 23NVR | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| Crystal Clear® 221 | Smooth-On, Inc | PUR, Unspecified | Crystal Clear® |
| Durolon® IR2500 CR010 | Unigel Plásticos | PC | Durolon® |