Geon™ HTX Ultra LA426G Black 2880
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ HTX Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EyZYEy_Geon-HTX-Ultra-LA426G-Black-2880.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon HTX Ultra LA426 has a higher gloss product. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 431311640000 | ASTM D4216 | |
| PVC Cell Classification | 13225 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 74 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1990 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 35.8 | MPa | ASTM D638 |
| Flexural Modulus | 1990 | MPa | ASTM D790 |
| Flexural Strength | 62.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 230 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 51.6 | J/cm | ASTM D4226 |
| 23°C 4 | 93.4 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 87.8 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm | 88.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 86.1 | °C | ASTM D648 |
| CLTE - Flow | 8.4E-5 | cm/cm/°C | ASTM D696 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Acceptable | ||
| 推荐在华氏160度下将材料干燥至少2小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 174 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Procedure A, C.125 Throwing |
| 4 . | Procedure B, C.125 Throwing |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sunny® PA66 EN400 | Guangdong Shunde Shunyan New Material Co., Ltd. | Nylon 66 | Sunny® |
| Texalan® 3 Series 372D | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 3 Series |
| Ferro PP LPP20BF39WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| KOCETAL® SO301 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| Plexiglas® SG10 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |