Hylex® P1025G10HB
| Category: | PC , Polycarbonate |
| Manufacturer: | Ravago Manufacturing Americas, LLC |
| Trademark: | Hylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EyThlN_Hylex-P1025G10HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate, High Flow, 10% Glass Filled |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 to 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.50 | % | ISO 294-4 |
| Water Absorption (24 hr) | 0.14 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 79.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.2 | % | ISO 527-2 |
| Flexural Modulus | 3620 | MPa | ISO 178 |
| Flexural Stress | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 7.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 132 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 128 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 16 | kV/mm | ASTM D149 |
| Arc Resistance | 120 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 305 TFE 15 SI 2 HB | RTP Company | PC | RTP |
| Styrolution PS 124N/L | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| TAROLOX GFR 4 | Taro Plast S.p.A. | PBT | TAROLOX |
| EcoBlend® HML5150 | Shanghai KumhoSunny Plastics Co., Ltd. | PLA+PMMA | EcoBlend® |
| LNP™ THERMOCOMP™ DF006LXN compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |