Lupoy® GP5006B
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EyI8y9_Lupoy-GP5006B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose, High Flow Application Miscellaneous Goods |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.14 | g/cm³ | ASTM D792 |
| -- | 1130 | kg/m³ | ISO 1183 1 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Melt volume-flow rate (260°C/5.0 kg) | 20.5 | cm³/10min | ISO 1133 2 |
| Molding Shrinkage - Flow (3.20 mm, Injection Molded) | 0.50 to 0.80 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.14 | % | ISO 62 3 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile modulus | 2000 | MPa | ISO 527-2 4 |
| Tensile Strength | |||
| Yield, 3.20 mm, Injection Molded 5 | 55.9 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2 6 |
| Tensile Strain | |||
| Yield | 5.5 | % | ISO 527-2 7 |
| Break, Injection Molded 8 | > 100 | % | ASTM D638 |
| Nominal strain at break | > 50 | % | ISO 527-2 9 |
| Flexural Modulus 10(3.20 mm, Injection Molded) | 2260 | MPa | ASTM D790 |
| Flexural Strength 11(3.20 mm) | 90.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 12 | ||
| -30°C | 18.0 | kJ/m² | |
| 23°C | 47.8 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 13 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm, Injection Molded | 290 | J/m | |
| 23°C, 3.20 mm, Injection Molded | 570 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm, Injection Molded | 114 | °C | ASTM D648 |
| 1.8 MPa | 109 | °C | ISO 75-2 14 |
| Glass Transition Temperature 15 | 140 | °C | ISO 11357-2 16 |
| Vicat Softening Temperature (50°C/h, B (50N)) | 129 | °C | ISO 306 17 |
| CLTE | ISO 11359-2 18 | ||
| Flow | 8.2E-5 | cm/cm/°C | |
| Transverse | 8.9E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 19 |
| Volume resistivity | > 1.0E+13 | ohms·m | IEC 60093 20 |
| Electric strength | 48 | kV/mm | IEC 60243-1 21 |
| Relative Permittivity (1 MHz) | 2.80 | IEC 60250 22 | |
| Dissipation Factor (1 MHz) | 0.010 | IEC 60250 23 | |
| Comparative tracking index | 275 | IEC 60112 24 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Rear Temperature | 240 to 270 | °C | |
| Middle Temperature | 245 to 275 | °C | |
| Front Temperature | 245 to 275 | °C | |
| Nozzle Temperature | 245 to 275 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | 50 mm/min |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | 50 mm/min |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | 10 mm/min |
| 11 . | 10 mm/min |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | 10 °C/min |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 22 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 23 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 24 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP QR678K | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® PP |
| SMOKEGUARD™ O 208 NATURAL | AlphaGary | Polyolefin, Unspecified | SMOKEGUARD™ O |
| TOTAL Polyethylene Lotrène® Q1018 H | TOTAL Refining & Chemicals | LLDPE | TOTAL Polyethylene |
| Clariant Nylon 6/6 6601-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| FLEXCHEM™ 4553 | Colorite Polymers | PVC, Flexible | FLEXCHEM™ |