HiFill® PA4/6 CF30
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | EyBap6_HiFill-PA4-6-CF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PA4/6 CF30 is a Polyamide 46 (Nylon 46) product filled with 30% carbon fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.31 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 1.9 | -- | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Break) | 228 | 179 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | 3.5 | % | ASTM D638 |
| Flexural Modulus | 16500 | 11000 | MPa | ASTM D790 |
| Flexural Strength | 365 | 283 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | 110 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 285 | -- | °C | ASTM D648 |
| CLTE - Flow | 2.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 10 | -- | ohms·cm | ASTM D257 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 282 to 316 | °C | |
| Middle Temperature | 282 to 316 | °C | |
| Front Temperature | 282 to 316 | °C | |
| Processing (Melt) Temp | 246 to 316 | °C | |
| Mold Temperature | 87.8 to 127 | °C | |
| Back Pressure | 0.00 to 0.345 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| New-prene™ 6050N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| AKROMID® B3 GF 25 1 L natural (4781) | AKRO-PLASTIC GmbH | Nylon 6+PP | AKROMID® |
| Diakon® TD642 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Enviramid® N1300STHL BK | Ravago Manufacturing Americas, LLC | Nylon 66 | Enviramid® |
| OnFlex™ S KA 40A-3S1767 | PolyOne Corporation | TPE | OnFlex™ |