Category: | ABS , Acrylonitrile Butadiene Styrene |
Manufacturer: | Polykemi AB |
Trademark: | POLYabs |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | ExfoZ6_POLYabs-N00-LG.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Low Gloss |
General Information | |
---|---|
Features |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.05 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ISO 1133 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow | 0.60 to 0.80 | % | |
Flow | 0.60 to 0.80 | % |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Stress | 44.0 | MPa | ISO 527-2 |
Flexural Modulus (23°C) | 2000 | MPa | ISO 178 |
Flexural Stress | 66.0 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength (23°C) | 17 | kJ/m² | ISO 179 |
Flammability | Nominal Value | Test Method | |
---|---|---|---|
Flame Rating (1.60 mm) | HB | UL 94 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
MarFlex® 9608XD | Chevron Phillips Chemical Company LLC | HDPE | MarFlex® |
Sup-tech A9000 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 66 | Sup-tech |
Akulon® K123, K123/A | DSM Engineering Plastics | Nylon 6 | Akulon® |
Exceed™ 2018KB | ExxonMobil Chemical | mPE | Exceed™ |
LEXAN™ EX9332T resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |