| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RJM International, Inc. |
| Trademark: | RJM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ExfO1e_RJM-SN601G30-F.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| RJM SN601G30-F is a Polyamide 66 (Nylon 66) product filled with 30% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Additive/Masterbatch. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 118 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 5880 | MPa | ASTM D790 |
| Flexural Strength | 245 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | 215 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toraycon® 1158W | Toray Resin Company | PBT | Toraycon® |
| TRIBOCOMP® POM CF10 TS0 | EPIC Polymers | Acetal (POM) Copolymer | TRIBOCOMP® |
| U-polymer UG-100-30 | UNITIKA Plastics Division | Polyarylate | U-polymer |
| ALTECH® PP-H A 2040/159 GF40 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Latiohm 75/4-08 PD01 G/30 | LATI S.p.A. | PBT | Latiohm |