Edgetek™ ET3500-5002 BK
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ExVGqg_Edgetek-ET3500-5002-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Edgetek™ Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1(23°C) | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/2.16 kg) | 17 to 22 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/21.6 kg) | 13.0 to 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.10 to 0.20 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm, Injection Molded) | 5900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C, 4.00 mm, Injection Molded) | 100 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C, 4.00 mm, Injection Molded) | 2.2 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C, Injection Molded) | 37 | kJ/m² | ISO 179 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 82.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | ±0.02 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA210SG30 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Spartech Polycom PP5930 B146 | Spartech Polycom | PP, Unspecified | Spartech |
| Europrene® 1723 | Versalis S.p.A. | SBR, Emulsion | Europrene® |
| LONGLITE® PMC T 385 J70 | CCP Group | Phenolic | LONGLITE® PMC |
| GELOY™ HRA170E resin | SABIC Innovative Plastics Europe | ASA | GELOY™ |