LNP™ THERMOCOMP™ JF003E compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ExCnTK_LNPTHERMOCOMPJF003Ecompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF003E is a compound based on Polyethersulfone resin containing Glass Fiber. Added features of this material include: Easy Molding. Also known as: LNP* THERMOCOMP* Compound JF-1003 EM Product reorder name: JF003E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 5950 | MPa | ASTM D638 |
| Tensile Strength (Break) | 101 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 5820 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 430 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 208 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8983-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Geon™ Vinyl Flexible R148CE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Kuraray K-Polymer KL-118 | Kuraray Co., Ltd. | PVOH | Kuraray K-Polymer |
| Sumiliteresin® PR-55291 | SBHPP | Phenolic | Sumiliteresin® |
| Sylvin 86039-85FUV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |